Material Properties|Innovacera

Material Properties|Innovacera

Product catalog summary

Material Properties Overview

This document provides a detailed comparison of various materials, focusing on their physical and mechanical properties. The materials include different types of Alumina (Al2O3), Silicon Carbide (SiC), Boron Carbide (B4C), and others.

Key Sections:

Density: The density of the materials ranges from 1.57 to 6 g/cm³, with specific values provided for each material type.
Color: The materials exhibit a range of colors including white, ivory, black, gray, and transparent.
Water Absorption: Most materials have 0% water absorption, indicating high resistance to moisture.
Vickers Hardness: Hardness values vary significantly, with some materials reaching up to 34.3 GPa.
Flexural Strength: The flexural strength at 20°C ranges from 50 to 1050 MPa, indicating the materials' ability to withstand bending forces.
Compressive Strength: Values range from 20 to 5000 MPa, showing the materials' resistance to compression.
Thermal Conductivity: Thermal conductivity values range from 1.4 to 110 W/m.K, affecting heat transfer efficiency.
Thermal Shock Resistance: Some materials can withstand temperature changes up to 605°C without damage.
Maximum Use Temperature: The maximum operational temperature ranges from 800 to 2450°C, depending on the material.
Electrical Volume Resistivity: Resistivity values indicate the materials' insulating properties, with some exceeding 10¹⁶ Ω.cm.

Notes:

Property values are typical and should not be considered as specifications.
Values are determined for test samples and should not be transferred to different formats or components.
Technical modifications are reserved by the company.

Contact Information:

XIAMEN INNOVACERA ADVANCED MATERIALS CO., LTD. provides these materials, with contact details for further inquiries.

Catalog excerpts

XIAMEN INNOVACERA ADVANCED MATERIALS CO.,LTD. Unit 4G,West Side, Lianchang Bldg, NO.6-8 Huli Avenue, Huli District, Xiamen, Fujian, China 361006 Tel: 0086 592 5589730 Fax: 0086 592 5589733 Email: [email protected] www.innovacera.com Material Properties Machinable Glass Y2O3-ZrO2 Ceramic (MACOR) (YPTZ) Color Water Absorption Vickers Gpa —— Hardness Flexural Strength (20° Mpa 50~100 C) Compressive Strength (20° Mpa 20~100 C) Thermal Conductivity W/m.K 3.1 (20°C) Thermal Shock Resistance (20°C) Maximum Use Temperature Volume Resistivity (25°C) Boron Nitride(BN) Boron Carbide (B4C) Silicon Carbide(SiC) Graphite HPBN White / White / Transparent Transparent Note: 1. Property Values are typical and should not be considered specifications 2. The measured values mentioned before were determined for test samples and are applicable as standard values. 3. The values indicated must not be transferred to arbitrary formats, componets or partsfeaturing different surface qualities. They must not be considered as a guarantee fro specific properties. We reserve the right of technical modifications. * Vicker Hardness (HV0.3)

Open the catalog to page 1

All Xiamen Innovacera Advanced Materials Co., Ltd catalogs and technical brochures

*Prices are pre-tax. They exclude delivery charges and customs duties and do not include additional charges for installation or activation options. Prices are indicative only and may vary by country, with changes to the cost of raw materials and exchange rates.

Brand list