• Very low hydrogen content after re-drying.
• Excellent mechanical properties.
• Deposit free from porosity, excellent slag detachability.

• AWS A5.1 E7018 H4
• EN ISO 2560-A E 42 4 B 32 H5

• AC, DC+

• All positions

• ABS, LR, BV, DNV, RINA, TÜV, CE

• C: 0.05
• Mn: 1.2
• Si: 0.4
• P: ≤0.020
• S: ≤0.015

• Yield Strength (MPa): ≥420
• Tensile Strength (MPa): 510-640
• Elongation (%): ≥24
• Impact ISO-V (J): -30°C: ≥27, -40°C: ≥47, -50°C: ≥70

• Diameter x Length (mm) and Current Range (A):
  • 2.5 x 350: 65-95
  • 3.2 x 350: 100-135
  • 3.2 x 450: 100-135
  • 4.0 x 350: 110-210
  • 4.0 x 450: 110-210
  • 5.0 x 450: 170-240

• 2.5 x 350: VPMC (28 electrodes, 0.6 kg), VPMD (90 electrodes, 1.9 kg), CBOX (195 electrodes, 4.2 kg)
• 3.2 x 350: VPMD (55 electrodes, 1.9 kg), CBOX (120 electrodes, 4.2 kg)
• 3.2 x 450: VPMD (54 electrodes, 2.4 kg), CBOX (120 electrodes, 5.3 kg)
• 4.0 x 350: VPMD (40 electrodes, 2.1 kg), CBOX (85 electrodes, 4.5 kg)
• 4.0 x 450: VPMD (40 electrodes, 2.7 kg), CBOX (85 electrodes, 5.7 kg)
• 5.0 x 450: CBOX (55 electrodes, 5.7 kg)

Test results for mechanical properties, deposit or electrode composition, and diffusible hydrogen levels were obtained from a weld produced and tested according to prescribed standards. Actual results may vary based on several factors including weld procedure, plate chemistry, and temperature. Users should confirm suitability through qualification testing or other appropriate means before use.