• The welding current can be reduced to low values while maintaining a stable arc, beneficial for gap-bridging.
• Excellent positional welding characteristics make CITOREX ideal for welder training.
• Low silicon content in the weld deposit makes it suitable for components that will be galvanized or enameled.

• AWS A5.1 E6013
• EN ISO 2560-A E 38 2 RB 12

• AC, DC-

• All positions except vertical down

• LR, BV, DNV, TÜV, DB

• C: 0.07
• Mn: 0.6
• Si: 0.2

• Condition: As welded (AW)
• Yield Strength: ≥330 MPa (AWS), ≥380 MPa (EN ISO)
• Tensile Strength: ≥430 MPa (AWS), 470-600 MPa (EN ISO)
• Elongation: ≥17% (AWS), ≥20% (EN ISO)
• Impact ISO-V at -20°C: Not specified (AWS), ≥47 J (EN ISO)
• Typical Values: Yield Strength 430 MPa, Tensile Strength 500 MPa, Elongation 28%, Impact 49 J

• Diameter x Length (mm): 2.5 x 350, Current Range (A): 50-90
• Diameter x Length (mm): 3.2 x 350, Current Range (A): 100-150

• Diameter x Length: 2.5 x 350, Packaging: CBOX, Electrodes/pack: 210, Net weight/pack: 4.1 kg, Item number: W000258269
• Diameter x Length: 3.2 x 350, Packaging: CBOX, Electrodes/pack: 130, Net weight/pack: 4.3 kg, Item number: W000258270

Test results for mechanical properties, deposit or electrode composition, and diffusible hydrogen levels were obtained from a weld produced and tested according to prescribed standards. Actual results may vary based on factors such as weld procedure, plate chemistry, temperature, weldment design, and fabrication methods. Users should confirm suitability through qualification testing or other appropriate means before use.