Plastic Metal 2-component epoxy adhesives
14Pages

Plastic Metal 2-component epoxy adhesives • durable • fast • economical

Plastic Metal WEICON Plastic Metal is ideal for providing fast, cost effective and durable repairs and coatings to many different types of material. WEICON Plastic Metal is also suitable for tool and mould making. After mixing the two components, WEICON Plastic Metal hardens at room temperature to a firm, metal-like material which immediately adheres to almost every kind of surface. Time of hardening depends on the type. Unlike polyester resin, the material does not shrink while curing. The cured material may be machined, e.g. • drilled • milled • ground • filed The range consists of 18...

In industrial design and manufacturing, WEICON Plastic Metal is used for making moulds and models, in particular • as an aid for making moulds for rubber and injection moulded parts • making dies • templates and models for pre-production testing • lining of cutting tool guides • making fixing devices. viscous - steel-filled temperature resistant from -35°C up to +120°C WEICON Plasic Metal is ideal for maintenance works and will give durable repairs without the need for expensive replacement parts. Holding device Due to its liquid consistency, WEICON Plastic Metal B is particularly suitable...

liquid - aluminium-filled high-temperature resistant from -35°C up to +220°C viscous - aluminium-filled temperature resistant from -35°C up to +120°C Filling of holes in an aluminium housing High-temperature resistant casting resin system especially for industrial use. This type is non-corroding, anti-magnetic and cures practically without shrinkage. The product provides high temperature resistance after precuring at room temperature and post-curing (afterbake) at +120°C. WEICON F2 is highly recommended for making castings and in particular for: Especially suitable for: • pouring out moulds...

liquid - mineral-filled - extremely wear resistant high temperature resistant from -35°C up to +180°C putty - mineral-filled - extremely wear resistant high temperature resistant from -35°C up to +200°C, briefly up to +260°C Repair of a feed impeller Blue, brushable surface protection with extremely high wear and abrasion resistance. Forms a smooth surface of low friction which shows a high chemical resistance and which is used: • for lining highly stressed pump cases • as a wear protection for slide bearing, slides, funnels and pipes • for repairing castings, valves and blower vanes Large...

putty - steel-filled - super-fast curing temperature resistant from - 35°C up to +90°C putty - titanium-filled - wear resistant - temperature resistant from - 35°C up to +200°C, briefly up to +260°C Emergency repair of a water pipe Repair of worn-out threads in elements of a mobile stand The universal type for quick repairs due to its fast-curing properties (pot life 5 minutes, may be machined after 45 minutes) and its simple application. This titanium-filled type is especially suitable for repairs which require high compressive strength and extreme chemical resistance. • for quick repairs...

liquid - steel-filled - wear resistant temperature resistant from -35°C up to +120°C putty - mineral-filled - wear resistant temperature resistant from -35°C up to +120°C Fixing device Coating of a stell plate in a potato peeling drum. Corundum particles are filled into the non-cured material This pourable wear-resistant type is used in mould making and wherever metal parts are subject to high wear caused by friction, e.g.: • for repairing and build-up of shafts • for pouring out bearings, cutting and punching tools • for making casting and profile milling models as well as drawing moulds •...

Technical Data WEICON Plastic Metal in non-cured condition Product type Composition Specific Properties Complete Packaging Sizes Mixing ratio (Weight %) Resin Density of the mixture g/cm³ Max. Cure times Viscosity layer in h of the thickness mixture per appli- mecha- final . cation (200 g preparation) mPa s nical hardmm loads ness Epoxy resin steel-filled Epoxy resin steel-filled Epoxy resin bronze-filled Epoxy resin aluminiumfilled liquid, high-temp. resistant Epoxy resin aluminiumfilled Epoxy resin aluminiumfilled Epoxy resin steel-filled putty, high-temp. resistant Epoxy resin...

WEICON Plastic Metal in cured condition Mean strength at +25°C acc. to DIN 53281-83 / ASTM D 1002 Product type Thermo forming resistance °C / °F Colour after curing Shore hardn. D (ASTM D 1706) transparent, slight inherent colour WEICON Epoxy Resin Putty WEICON Casting Resin MS 1000 Conversion factors: (°C x 1.8) +32 = °F • kV/mm x 25.4 = V/mil • mm / 25.4 = inches • µm / 25.4 = mil • N x 0.225 = lb • N/mm x 5.71 = lb/in • N/mm x 5.71 = pli • N/mm² x 145 = psi • MPa x 145 = psi • MPa x 0.145 = KSI • mPa.s = cP • N.m x 8.851 = lb.ft • N.m x 0.738 = lb.ft • N.mm x 0.142 = oz.in • kg x 2.2046...

Pot life and processing time The indicated pot life times refer to mixtures of 200 g and +20°C material temperature. Larger quantities will cure faster due to the typical heat reaction of epoxy resins. WEICON Plastic Metals should be processed at room temperature (approx. 20°C). Pot life and cure time will be reduced at higher temperatures. The rule of thumb is: Every increase of 10°C above room temperature leads to a reduction of pot life and cure time by 50%. At temperatures below +16°C, the pot life and cure time will slow down; below approx. +5°C no reaction between resin and hardener...

Supplementary Range WEICON Sealant and Adhesive Remover WEICON Sealant and Adhesive Remover dissolves and quickly eliminates sealant and hardened adesive residues, as well as lacquers and paints, even on vertical surfaces. Repair of a water-cooled turbocharger housing Applications • dissolves all types of sealant residues from cylinder heads, oil pans, water pumps, exhaust manifolds, valve covers and gear flanges • reliably removes carbon residues, paints and lacquers • eliminates oils, resins, greases and tar • removes all kinds of adhesive, even hardened cyanoacrylate and anaerobically...