MATERIAL DATA SHEET PLASTIC PARTS Material data sheet for plastic parts PLASTIC Base material Binder - type Tensile strength Yield point Burn - out temperature Residual ash content Especially suitable for Advantages PMMA particulate material (55 pm) Polypor B (PPB) > 2,0 MPa 1 % 700 °C < 0.01 % weight investment casting; design models sharp edges; for highest accuracy and true-to-detail; reusable particle material PMMA particulate material (85 pm) Polypor C (PPC) >2,0 MPa 1 % 600 °C < 0.01 % weight investment casting; architectural models burns out well with practically no residual ash content; reusable particle material TECHNICAL DATA PLASTIC PARTS SUITABLE FINISHING TREATMENT Layer thickness Standard 150 pm Wax Epoxy Resolution x, y up to 600 dpi Tensile strength see base material up to 25 MPa Burn-out temperature see base material - Characteristics smooth liquid- solid material, resistent surface dyeable Model sizes up to 1,000 x 600 x 500 mm (LxWxH) up to 600 dpi print resolution Same handling as for conventional wax parts after wax infiltration No shell cracking due to negative coefficient of thermal expansion. Suitable for autoclaves, even for thin-walled shells Low residual ash content No heat distortion as hardening process is purely a chemical process Coloured display models through epoxy infiltration Warranty/Disclaimer: The performance characteristics of these products may vary according to every individual case. voxeljet assumes no liability for the actual marketability of the products, as well as for the applicability of the products in individual cases. ©voxeljet. All rights reserved. The designations voxeljet, VX200, VX500, VX1000, VX2000 and VX4000 are registered trademarks of voxeljet AG. Specifications subject to change without notice. Validity: 01/2018. Specifications are subject to change without notice. voxeljet is ISO 9001 - certified. voxeljet AG Paul-Lenz-StraBe 1a 86316 Friedberg Germany Tel +49 821-74 8 3-100 Fax +49 821-74 83-111 [email protected] www.voxeljet.com Americas EMEA AsiaPacific