Technical UltiMaker Technical data sheet — Ultimaker Nylon

Open the catalog to page 1
Nylon - 2

Injection molding Typical value Test method Tensile modulus Tensile stress at yield Tensile stress at break Elongation at yield Elongation at break Flexural strength Flexural modulus Izod impact strength, notched (at 23°C) Charpy impact strength (at 23°C) Hardness Test method ISO 527 (1 mm/min) ISO 527 (50 mm/min) ISO 527 (50 mm/min) ISO 527 (50 mm/min) ISO 527 (50 mm/min) ISO 178 ISO 178 ISO 180 Thermal properties Melt mass-flow rate (MFR) Heat deflection (HDT) at 0.455 MPa Heat deflection (HDT) at 1.82 MPa Glass transition Coefficient of thermal expansion Melting temperature Thermal...

Open the catalog to page 2
Nylon - 3

Notes Properties reported here are average of a typical batch. The 3D printed test specimens were printed in the XY plane, using the normal quality profile in Cura 2.1, an Ultimaker 2+, a 0.4 mm nozzle, 90% infill, 250 ˚C nozzle temperature and 60 ˚C build plate temperature. The values are the average of 5 transparent and 5 black specimens for the tensile, flexural, and impact tests. The Shore hardness D was measured in a 7-mm-thick square printed in the XY plane, using the normal quality profile in Cura 2.5, an Ultimaker 3, a 0.4 mm print core and 100% infill. Ultimaker is constantly...

Open the catalog to page 3

All Ultimaker catalogs and technical brochures

  1. PLA

    3 Pages

  2. Breakaway

    2 Pages

  3. Ultimaker 2+

    4 Pages

  4. Ultimaker 3

    4 Pages