Ballistics material handbook

Yarn List Twaron ballistic yarns Linear Density Filaments Twaron-Type Dtex (effective) No. Strength at Break Tenacity at Break Elongation at Break Chord Modulus The history of protecting man against weapons goes back to ancient times. For hundreds of years, metal materials have been used not only for body armor but also for the protection of larger objects such as vehicles, providing what is called ‘hard protection‘. N mN/tex % GPa 2.350 3.5 91 3.5 100 420 (415) 500 550 1000 2040 105 Microfilament 550 (570) 500 2040 135 Microfilament 2.350 840 (860) 1000 2000 215 Microfilament 2.500 930...

Twaron ballistic fabrics Twaron yarn cross sections Recently, Teijin Aramid introduced the world’s finest filament yarn called Twaron 550f1000. This Whenever the combination of high functionality, comfort and economy is required, enhanced tenacity, ultra microfilament yarn enables the production of very lightweight ballistic you will find advanced para-aramid Twaron yarns being used in sophisticated fabric vests and is available in 550dtex with 1000 filaments. constructions tailored for specific end uses. In general, ballistic threats emanate either from bullets or fragments. Bullets can be defined...

A wide variety of solutions The range of ballistic fabrics covers different key attributes and characteristics: CT 612 Key attributes/characteristics • 25 g/m 1 ballistic fabric, based on one of the thinnest yarns ever made in the para-aramid spinning process • edicated to providing maximum protection against bullets D and fragments • uccessfully used in military vests, providing a lightweight and S comfortable solution • vailable in Water Repellent Treated (WRT) finish or loom state A CT 716 2 550 dtex Primary application Body armor CT 704 840 dtex Primary application Key attributes/characteristics...

Cross sections T 760 3360 dtex Primary application Key attributes/characteristics • 35 g/m² ballistic fabric 6 • eavy and very flexible fabric for up-armoring of vehicles H • xcellent shaping possible, therefore suitable for manufacturing E Cross sections of fabrics (200g/m2) containing standard aramid yarn (upper part) and Twaron microfilament yarn (lower part) process Hard Ballistics Microflex Key attributes/characteristics • 20 g/m 2 ballistic fabric, dedicated to providing maximum protection to correctional officers • patented puncture-resistant fabric made from Twaron A microfilament yarn,...

Twaron LFT SB1 Twaron UD41 The past years have brought many improvements in ballistic protection materials. Today’s lightweight protective vests need to meet a complex set of requirements, including Teijin Aramid’s approach, combining low-crimp woven products with low resin content, both bullet and stab protection. Solutions based on Twaron Unidirectional Laminate UD41 has resulted in Twaron Laminated Fabric Technology SB1 (LFT SB1) – a thin, very flexible – or those combining UD41 with other Twaron materials – offer several advantages for laminate comprising two fabric layers sandwiched with...

Twaron LFT-AT/AT Flex Twaron Sideguard® The primary objective of a ballistic pack is clear – to stop the bullet. But in a number of In the past, thickly layered and quilted ballistic fabrics provided protection against bullets situations, the resultant blunt trauma remains an obvious and unwelcome problem. and shrapnel (hot weapons), but not against blades, knifes and needles (cold weapons). The answer was the next generation of laminate technology - specially coated, layered In light of this, Teijin Aramid Ballistic Engineering has developed a material permitting an fabrics that could prevent...

Twaron for stabbing protection Twaron ladies’ vest Twaron SRM® While the advancement of aramid yarns and fabrics has resulted in an ever-improving level Along with the need for protection against ballistic impact, protection against attacks by of protection performance, progress on the comfort side failed for a long time to sharp and pointed weapons has become a matter of increasing priority. In more and more acknowledge the special needs of female wearers. Although the number of female officers countries, police officers are facing the growing threat of a wide range of stabbing weapons. has...

Endumax Twaron in hard ballistic protection Today’s police and defense forces rely increasingly on advanced digital and communications A wide range of materials are used for different hard ballistic applications. technology, and their equipment needs are changing accordingly. In addition to requiring These materials include ceramics, special metal alloys, honeycomb structures and even improved ballistic protection, they now need to carry more equipment into daily service. simple car-body steel combined with Twaron fabric. Thousands of firing and blasting tests This does not mean, however, that...

Fabric List Style Linear Density TwaronType Ballistic laminates (LFT) / coated fabrics Weave Set Set [per 10 cm] [per inch] Areal Density [dtexnom] [g/m2] Warp/Weft Warp/Weft CT 612 550 f 500 2040 CT 613 550 f 500 CT 704 Thickness [mm] [oz/yd2] Warp Weft Warp 110 110 28 28 125 3.69 2040 Plain 123 123 31 31 135 840 f 1000 2000 Plain 107 107 27 27 CT 706 840 f 1000 2000 Plain 126 126 32 CT 707 930 f 1000 2040 Plain 85 85 CT 709 930 f 1000 2040 Plain 105 CT 714 1100 f 1000 2040 Plain CT 716 1100 f 1000 2040 CT 732 1680 f 1000 CT 736 [N/5cm x 1.000] Weft Plain Minimum Breaking Strength Minimum Breaking...

www.teijinaramid.com or e-mail us at: [email protected] 38-14-05/2012 About Teijin Aramid We are Teijin Aramid, a subsidiary of the Teijin Group with a passion for aramid. Our commitment both to our products and to our customers has made us a global leader in aramids. Wherever strength, safety, heat or flame resistance, low weight or sustainability is required, you will find our Twaron®, Sulfron®, Teijinconex® or Technora®. Our products are used worldwide in many different applications and markets, including automotive, ballistic protection, marine, civil engineering, protective clothing,...