Technical data sheet TDS SSI Version 3.3 Revision : 03.02.2021 Silcrete SSI — Standard Industrial Floor System Self-leveling industrial floor. Hardens fast and tension-relieved with a layer thickness of 2 - 50 mm. Eco-Binder technology environmentally friendly mineral very low emission EC 1PLUS fast curing and tension-relieved waterproof up to 1.5 bar fulfills the requirements for conductivity according high flowability high abrasion resistance easy application also processible by machine • for revision of concrete and screed • as coating for areas with high mechanical load like garages, warehouses und production areas • walkable after 4 hours • applicable in layer thicknesses of 2 - 50 mm, for larger areas a layer thickness of approx. 3 - 5 mm is • Cement and calcium sulfate-based screed, heated and non-heated • Self-leveling compounds, floor filling compounds • Adhering ceramic coverings Prior to coating, ensure that the surface is stable and has sufficient surface tensile strength. The surface should also be ready for coating, dry or matt damp, clean and free from all kinds of debris. Mechanical surface preparation e.g. shotblasting is recommended. Due to roughening the surface, the adhesion for the subsequent layer can be improved. Deeper ruptures must be filled with Silcrete MV 035. The surface should be permanently vibration-free and crack-free. Therefore, new concrete or screed should have a minimum age of 28 days. Already existing cracks must be repaired professionally. The adhesive strength of the substrate must be at least 1.5 N/mm2. The substrate has to be dry for priming, and dried for 2 hours after priming with Silcrete SSI PRIM. By priming the surface, the absorbency of the substrate is adjusted. This avoids the rising of air bubbles during the subsequent coating. In order to guarantee this on critical undergrounds, a test area of 1m2 should be created. Apply a further layer of primer if necessary. The coating work on the primer has to be finished within 6 hours. Please refer to the technical data sheet of Silcrete SSI PRIM for more information. The edge joint must be prepared

Technical data sheet TDS SSI Version 3.3 Revision : 03.02.2021 with a suitable expansion strip. Thereby attention must be paid to a clean adhesion to avoid material flowing below or behind the expansion strip. Expansion joints must be adopted. After finishing all coating works, all joints have to be filled with a permanently elastic compound. Transitions and closing edges should be protected against over- flow by installing end rails. For coatings on tiled floors the surface has to be pre-leveled with Silcrete SSI. For this purpose, Silcrete SSI is applied by a toothed spatula or a screed rake....

Technical data sheetTDS SSI Version 3.3 Revision : 03.02.2021 timely manner for a proper and promising evaluation by Revoxia. Any further details regarding the application of our products have to be confirmed in writing by Revoxia. The customer must test the product's suitability for the intended application and purpose. We reserve the right to change the product specifications due to the ongoing development. Apart from that our general terms and conditions are valid. This data sheet supersedes all earlier technical data on this product. The technical data sheet can be requested on [email protected]...