Daylight Magna High Tensile

Daylight Magna High Tensile
2Pages

Catalog excerpts

Technical Data Daylight Magna High Tensile Phone case Compatible Printers Properties Tensile Modulus Low Liquid Crystal Shore Hardness Soft Colours White Introduction Photocentric’s Daylight Magna High Tensile formulation has been created for producing parts exhibiting exceptional tensile strength and elongation comparable to acrylics and polyimides. Printed parts cannot be deformed or compressed easily, while having minimal shrinkage and high accuracy. Best Used for: • • • Engineering Prototyping Tooling and moulds Unique Features: • • • • • High tensile modulus High accuracy Smooth surface finish Minimal shrinkage Heat deflection temperature of 95°C UK Titan House, 20 Titan Drive, Peterborough, PE1 5XN. email: info@photocentric.co.uk USA Avondale 107 - Building ‘A’ 855 N. 107th Ave., Suite A110, Avondale, Arizona 85353 email: info@photocentricusa.com www.p

Open the catalog to page 1

Technical Data Post Processing Processing Instructions • To print with Photocentric Liquid Crystal Magna, choose ‘High Tensile White’ and the desired layer thickness when preparing your print file in Photocentric Studio. It is recommended to print models which do not take longer than 12hrs to print at 100 µm layer thickness or build height no greater than 150mm at any desired layer thickness. Heat the resin to 30°C in the bottle. Shake the resin bottle for 2 minutes before pouring into the resin vat. Parts can be washed in 15 minutes using Photocentric Resin Cleaner or alternatively, in 10...

Open the catalog to page 2

Daylight Magna High Tensile 2Pages

Catalog excerpts

All Photocentric Group catalogs and technical brochures

Daylight Magna High Tensile
2Pages