CRUCIBLESTANDS MUFFLERINGS CRUCIBLECOVERS EXCEL and HIMELT are high quality carbon-bonded silicon carbide crucibles manufactured using the latest roller-forming techniques and are designed to cater for a range of non-ferrous melting applications. > Excel E is a high quality carbon-bonded silicon carbide crucible manufactured using the latest roller-forming techniques and incorporating a special multi-phase glaze protection system.This product range is designed for aluminium melting andholding applications. INDUX is a high quality ceramic bonded clay graphite crucible range manufactured to provide controlled graphite alignment and optimised electrical properties to suit specific frequency ranges for induction melting applications. ISO-ALUSTAR is a premium quality crucible manufactured by high pressure iso-static pressing and incorporating high levels of oxidation resistance and mechanical durability.This product range is designed to provide superior resistance toattack by melt treatment agents typically used in aluminium alloy applications. SALAMANDER SUPER is a high quality ceramic bonded clay graphite crucible range manufactured by plastic forming techniques. INDUCTION FURNACES: Small Salamander Super crucibles aresometimes used in medium to high frequency induction furnaces > SALAMANDER SUPER crucibles are used to provide consistent performance in fuel-fired furnaces and medium / high frequency induction furnaces. The smaller sizes are typically used to melt precious metals, while larger sizes can be used for some ferrous alloys such as grey iron as well as to melt non-ferrous alloys. EXCEL is intended for aluminium melting in oil-fired furnaces, melting copper-based alloys in gas and oil-fired furnaces, melting precious metals and non-ferrous allys in low to medium frequency induction furnaces. HIMELT provides enhanced performance in those applicationswhere more arduous service conditions exist. > INDUX crucibles are used to provide consistent performance in medium frequency induction furnaces. INDUX L crucibles are designed for furnaces operating at 1 Ֆ 2 kHz. INDUX H crucibles are suited to furnaces operating at frequencies from 3kHz and upwards. INDUX crucibles are typically used to melt copper alloys and precious metals. EXCEL E is used for melting, holding and melt/holding of aluminium alloys in electric resistance and gas-fired furnaces. > ISO-ALUSTAR offers superior performance for aluminium holding and melting in electric resistance and gas furnaces, as well as melting and holding of zinc and zinc alloys. > SPOUTEXTENSIONS LAUNDERS HOTROD PYROMETERSHEATHS ЕFast melting speed through high consistent thermal conductivityHigh resistance to oxidationՕExcellent Thermal Shock resistanceEnergy efficient > ՕClean meltingGood thermal conductivityՕGood resistance to chemical corrosion High refractoriness INDUCTION FURNACES: The heat-up procedure is dependant onfurnace frequency, coil dimensions, and the resistivity of the metal being melted. It is recommended where possible to preheat the crucible empty. The power input rate should initially be limited until the crucible becomes bright red over its entire surface. The time taken to pre-heat will depend on the size of the crucible, but is usually in the range 20 Ֆ 40 minutes. Once one third of the crucible is full of molten metal the power can be increased to a higher level. Silicon carbide crucibles absorb proportionally high levels of power from the induction field. Care should be taken not to overheat the crucible. The actual maximum power setting should be assessed from experience and will be dependant on the capacity of the crucible. The appearance of the inside wall of the crucible should be monitored for signs of over-heating and the power reduced once the full charge is molten. > Fast melting speed through high consistent thermal conductivityՕExcellent thermal shock resistance High resistance to oxidationՕGood erosion resistanceGood resistance to corrosive attack by chemical treatmentagents ՕControlled electrical resistivityGood thermal conductivityՕGood resistance to chemical corrosion High refractoriness > ՕExcellent resistance to attack by chemical treatment agentsHigh mechanical strengthՕExcellent resistance to oxidation High consistent densityՕFast melting speed through high thermal conductivity FUEL-FIRED FURNACES: Crucibles should be pre-heated emptyuntil they reach a uniform bright red colour (circa 900C) in order to pre-condition the glaze. The pre-heating time will depend on the size of the crucible. In the case of large capacity crucibles and furnaces with high output burners the rate of temperature rise should be controlled in the initial stages to minimise thermal stress. The typical time taken from ambient to red heat is up to 1hour. Avoid direct flame impingement on the crucible surface. > ELECTRIC RESISTANCEAND GAS FIRED FURNACES: Cruciblesshould be pre-heated empty. A new crucible should initially be heated slowly to 200аC over a period of two hours to eliminate any moisture that may be present. Subsequently the crucible should be heated to 600C on low power before the full heating rate is used to reach 950аC, or the desired working temperature if higher. Iso-Alustar crucibles used for holding applications should be held at 950C for one hour in order to fully develop the anti-oxidant glaze system. The time taken to reach temperature will depend on the size of the crucible but will typically be in the range two and a half to three hours. Avoid direct flame impingement on the crucible surface.The same heat up procedure should be repeated prior to re-useafter a cool-down period. The two hour drying period can be omitted except where the crucible has not been used for a long period in which case moisture that has been absorbed by slag will need to be slowly removed. > ELECTRIC RESISTANCEFURNACES: Crucibles should be pre-heate d PUSH-UP/DROP COIL FURNACES: The heat-up procedure isdependant on furnace frequency, coil dimensions, and the resistivity of the metal being melted. 3kHz furnaces: It is recommended where possible to preheat thecrucible empty. The furnace should initially be run at 20% of maximum power until the crucible shows signs of red heat. After 30minutes the power can be increased to 50% of the maximum. Loosely charge the crucible with metal and maintain the power level at 50% until approximately half the crucible contains molten metal. The power should then be increased to maximum.1kHz furnaces: The power absorption of the empty crucible maybe too poor therefore it may be necessary to pre-heat with a charge loosely in place in order to provide supplementary heating by conduction from the metal charge. Run the furnace at 20% of maximum power until the crucible shows signs of red heat. If after ? hour the crucible shows no evidence of red heat, increase the power to 50% of maximum. Hold at 50% until half the crucible contains molten metal, then increase to maximum power.Tilting furnaces: INDUX crucibles will be prone to thermal shockif the rate of temperature rise of the metal charge is too rapid. It istherefore recommended that where possible the crucible is pre-heated empty from cold using a maximum of 100Kw, or 50% ofmaximum power, whichever is smaller. Heat the crucible until it becomes bright red. This should take between 20 and 40 minutes. Once the metal charge is added the crucible itself will absorb very little power and will remain at red heat until the metal melts. On subsequent cycles the preheat procedure is unnecessary when the crucible is still red hot. > EXCEL E crucibles are coloured green and utilise the patterncoding X E. e.g. BX401E SALAMANDER SUPER crucibles are coloured black except forcertain smaller sizes that are supplied unpainted. empty on full power until they reach a uniform bright red colou r > Morganite manufactures a full line of accessories to complement its extensive crucible range. Excel E Accessories:650 - 1000аC (1202 - 1832F)Excel Accessories:900 - 1400аC (1652 - 2552F)Salamander Accessories:1000 - 1600аC (1832 - 2912F) (circa 900аC) and held at this temperature for 30 minutes in ord e INDUX crucibles are coloured black and utilize the suffix INDL orINDH to denote the specific type. > to pre-condition the glaze. The crucible can then be charged an d > EXCEL crucibles are coloured dark red and utilise the code X. e.g. AX800.HIMELT crucibles are coloured bright red and utilize the code HMe.g. AHM800 > the controller adjusted to achieve the desired operatingtemperature. ISO-ALUSTAR crucibles are finished green and utilise patterncoding with the suffix ALUS e.g. BN500ALUS > Excel E crucibles are available in a comprehensive range of shapes and sizes to suit most end user requirements. Custom sizes can be supplied by special request. Pyrometer hole in the wall and pyrometer pocket configurations are available to facilitate accurate measurement of metal temperature. A selection of fixed pouring spouts with optimised profiles is offered where required for tilting furnace applications. Excel E crucibles can be supplied with Morganites unique PDcoating system, which can assist with metal cleanliness and prevention of dross adhesion. > SALAMANDER SUPER crucibles are available in a range of sizes as A-shapes, F-shapes (bilge), and E-shape cylinders to suit a wide spectrum of end user requirements. Ladle liners are also available in standard or bottom pour configuration. Crucible Accessories: GAS FIRED FURNACES: Crucibles should be pre-heated emptyuntil they reach a uniform bright red colour (circa 900ҰC) and held at this temperature for 30 minutes in order to pre-conditio > INDUX crucibles are available in a range of sizes as A-shapes, F-shapes (bilge), and E-shape cylinders.Contact Morganite for a specific recommendation based on yourfurnace specification Crucible StandsՕMuffle Rings (rings increase the cold charge capacity of the crucible and can improve melt times)Crucible Covers ՕSpouts and Spout ExtensionsCrucible Lifters ՕOptimised glaze coatings tailored for specific temperaturerangesExcellent thermal conductivity and shock resistance ՕHigh resistance to oxidationGood wear resistanceՕGood resistance to corrosive attack by chemical treatmentagentsConsistent performanceՕHigh refractoriness Non-wetting properties n > . the glaze. The crucible can then be charged and the controller adjusted to achieve the desired operating temperature.The time taken to reach temperature will depend on the size ofthe crucible. In the case of large capacity crucibles and furnaces with high output burners the rate of temperature rise should be controlled in the initial stages to minimise thermal stress before applying the full power of the burner. Avoid direct flame impingement on the crucible surface. ISO-ALUSTAR crucibles are available in a range of shapes and sizes to suit most end user requirements. Certain sizes can be made available with pyrometer pocket configuration to facilitate accurate measurement of metal temperature. A selection of fixed pouring spouts with optimised profiles is offered where required for tilting furnace applications. The heat-up procedure is dependent on furnace frequency, coil dimensions, and the resistivity of the metal being melted. It is recommended where possible to preheat the crucible empty. The furnace should initially be run at 20% of maximum power until the crucible shows signs of red heat. After 30 minutes the power can be increased to 50% of the maximum. Loosely charge the crucible with metal and maintain the power level at 50% until approximately half the crucible contains molten metal. The power should then be increased to maximum. > EXCEL and HIMELT crucibles are available in a comprehensive range of shapes and sizes to suit most end user requirements. Custom sizes can be supplied by special request. Heavy wall (HW) versions can be supplied for increased life in arduous applications and a selection of fixed pouring spouts with optimised profiles is offered where required for tilting furnaces. EXCEL and HIMELT crucibles can be supplied with MorganiteՒsunique PD coating system, which can assist with metal cleanliness and prevention of dross adhesion. SALAMANDER SUPER crucibles are manufactured from premium grade raw materials to ISO9000:2000 quality standards. > Foundry Products * : INDUX crucibles are manufactured from premium grade raw materials to ISO9000:2000 quality standards. Hot Rod Pyrometer Sheaths ՕLaunders and TubesLadle BowlsՕDegassing TubesPlunger Mixers and Plunging BellsՕCements and Castables Plates and TilesՕNeedle Valves and Nozzles/Down Spouts > FUEL-FIRED FURNACES: Anew crucible should be pre-heatedempty in order to minimise the temperature gradient across the crucible wall. If the furnace refractories have been repaired or if there is a risk of the crucible having absorbed some moisture, then the furnace should initially be heated slowly up to circa 200C and held at this temperature until all moisture has been driven off. Anew crucible should initially be heated slowly and evenly to600ںC on low power, avoiding local impingement of flame. Subsequently the full heat input rate should be utilised to achieve a uniform bright red condition over the whole crucible (circa 900C / 1650ںF) at which point the crucible should be charged immediately taking care to avoid packing metal tightly orbridging ingots across the crucible. The furnace controls can then be set to achieve the desired metal operating temperature and heating should continue at the full rate until the metal has reached the desired temperature.In the case of crucibles to be fed with molten metal, it isimportant that the crucible body temperature is equivalent to or slightly above that of the molten metal in order to minimise thermal stress. > ISO-ALUSTAR crucibles are manufactured from premium grade raw materials to ISO9000:2000 quality standards. Assoon as the crucible has been pre-heated as specified, charge and melt immediately. Charge light scrap and returns first in order to form a cushion for heavier material. Use tongs to charge ingots and place large pieces and ingots vertically allowing space for expansion. Only add flux once the metal is molten and use the minimum quantity required to obtain good metal quality. EXCEL E crucibles are manufactured from premium grade raw materials to ISO9000:2000 quality standards. > Follow the specified preheat procedure. Charge light scrap and returns first in order to form a cushion for heavier material. Use tongs to charge ingots and place large pieces and ingots vertically allowing space for expansion. Only add flux once the metal is molten As soon as the crucible has been pre-heated as specified, charge and melt immediately.Charge light scrap and returns first in order to formacushion for heavier material. Use tongs to charg > As soon as the crucible has reached the specified pre-heat temperature, charge and melt immediately. Charge light scrap and returns first in order to form a cushion for heavier material. Use tongs to charge ingots and place large pieces and ingots vertically allowing space for expansion. Only add flux once the metal is molten. > e Crucible accessories are manufactured from premium grade rawmaterials to the same ISO9000:2000 quality standards as our crucibles. EXCEL and HIMELTcrucibles are manufactured from premium grade raw materials to ISO9000:2000 quality standards. > ingots and place large pieces and ingots vertically allowing spac e As soon as the crucible has been pre-heated as specified, charge and melt immediately. Charge light scrap and returns first in order to form a cushion for heavier material. Use tongs to charge ingots and place large pieces and ingots vertically allowing space for expansion. Only add flux once the metal is molten and use the minimum quantity required to obtain good metal quality. for expansion. Only add flux once the metal is molten and use the minimum quantity requiredto obtain good metal quality. > *Detailed information on these products is available by request Proper safety clothing must be worn at all times. Ensure that no moistureis introduced into the melt and that all refractories and tools aredry before coming into contact with molten metal. Provision should be made underneath the furnace to catch metal that may be discharged. > Excel E stands and muffle rings are used in conjunction with Excel E and Iso-Alustar crucibles for aluminium alloy and zinc applications in electric resistance and gas-fired furnaces. EXCEL stands and muffle rings are used in conjunction with Excel, Hi-Melt and Ultramelt crucibles intended for copper alloy and precious metal applications in gas and oil-fired furnaces.SALAMANDER crucible accessories are available as spoutextensions to increase pouring length and covers to exclude impurities from the melt. In addition a comprehensive range of graphitic Foundry products are offered in the form of both shaped and packaged refractories. We also supply crucible lifidi >