JETFINE® 1
4Pages

A simple, cost-effective, natural alternative to opaque polymers • Formulation guidelines at different PVCs

INTRODUCTION By reformulating as demonstrated in the following examples, the opaque polymer can quite simply be totally replaced by 60% Jetfine® 1 and 40% water, resulting in more cost-effective formulations with equivalent performance. FORMULATION AT PVC 43.8% Formulation, weight % Opaque polymer Formulation, properties Opaque polymer Spreading rate (m²/L) @ 98 opacity (ISO 6504-3) Scrub resistance class (ISO 11998) Opaque polymer Vinyl acetate copolymer, 50% Cracking: application on plaster board @ 300 to 1500µm wet film thickness Cost saving per litre* *subject to opaque polymer price...

Formulation, weight % Opaque polymer Formulation, weight % Opaque polymer Opaque polymer Vinyl acetate copolymer, 50% Formulation, properties Opaque polymer Vinyl acetate copolymer, 50% Spreading rate 0.0 m²/L @ 98 3.0 opacity Formulation, Opaque ® Scrub resistance, polymer GlossWith 85° Jetfine 1 properties class Krebs viscosity (KU) Spreading rate (m²//L) @ 98 opacity (ISO 6504-3) Spreading rate (m²/L) @ 98 opacity (ISO 6504-3) Scrub resistance class (ISO 11998) Scrub resistance class (ISO 11998) Cracking: application on plaster board @ 300 to 1500µm wet film thickness Cracking:...

Formulation, weight % Opaque polymer Opaque polymer Viscosity, KU Spreading 12.0 rate m²/L0.0 @ 98 opacity 2.4 L* Brightness Opaque polymer Spreading rate Vinyl acetate copolymer, 50% @ 98 m²/L Total opacity Vinyl acetate copolymer, 50% Scrub resistance, Formulation, class properties Opaque polymer Scrub resistance, 9.2 class Scrub resistance class (ISO 11998) Cracking: application on plaster board @ 300 to 1500µm wet film thickness Cost saving per litre* Formulation, properties Spreading rate (m²/L) @ 98 opacity (ISO 6504-3) *subject to opaque polymer price Opaque polymer Spreading rate...