MI 00 601

Product catalog summary

Material Overview: The MI 00 601 is a molded friction material characterized by a medium to high friction coefficient, reinforced with metal particles. It is noted for its low to medium wear and quiet operation. The material is easily cut, even in thick sections, and is composed of phenolic resins, short fibers, metal particles, and fillers.

Friction Properties: The static friction coefficient at 15 bar is 0.55±0.05 μ, increasing to 0.60±0.05 μ at 100ºC. Dynamic friction coefficient and wear rate are detailed in accompanying charts. The material exhibits a temperature fading threshold above 340 °C.

Physical Properties: The hardness is measured at 78±5 Shore-D (DIN53505), with a specific gravity of 1.80±0.05 gr/cm3 (ASTM D792) and an ignition loss of 43±2% (ASTM D7348).

Mechanical Properties: The tensile strength is 10±2 N/mm2 (ASTM D638), compressive strength is 100±5 N/mm2 (ISO 844:2014), Poisson's coefficient is 0.18±0.03, and Young's modulus is 2500±100 N/mm2 (ASTM D638).

Recommended Working Values: The maximum continuous operation temperature is 250 °C, while the maximum intermittent operation temperature is 350 °C.

Additional Recommendations: The recommended mating surface is perlitic cast iron with a hardness of HB150-200. Thermosetting adhesives are suggested for bonding. It is noted that rubbing speed, temperature, and pressure are interrelated, and changes in one will affect the others. The provided values represent typical conditions but are not the ultimate limits of the material.

Catalog excerpts

MI 00 601 Il Materiale MI 00 601 ha un medio/alto coefficiente di attrito rinforzato da polveri metalliche. Questo materiale ha una bassa/ media usura e risulta molto silenzioso durante l’utilizzo. Si presta facilmente al taglio anche per spessori elevati. MI 00 601 is molded Friction Material with a medium high friction coefficente reinforced with metal components. MI 00 601 it’s really silent during the used. Composition:The material consist phenolic resins, short fibres, metal particles and filler. Dati Tecnici / Technical Data Friction propieties (according graphics) Static Friction Coeﬃcient (15bar, from box): Static Friction Coeﬃcient (15bar, 100ºC): Dynamic Friction Coeﬃcient: Wear Rate: Physical properties Hardness (DIN53505): Speciﬁc Gravity (ASTM D792): Ignition Loss (ASTM D7348): Mechanical properties Tensile Strength (ASTM D638): Compressive Strength (ISO 844:2014): Poisson Coeﬃcient (ASTM D638): Young Modulus (ASTM D638): Recommended Working Values T° Max. Continuous Operation: Others Recommended Mating Surface: Recommended Adhesives: Perlitic cast iron, hardness HB150-200 Thermosetting adhesive Rubbing speed, temperature and pressure are related. Changing any values will change other. The values shown represent typical conditions, but are not ultimate limits of the material.

Open the catalog to page 1

All IMA BRAKE SYSTEMS AND FRICTION MATERIAL INDUSTRY catalogs and technical brochures

SWR
1 Page
RCI 21
1 Page
TAM 01
1 Page
Company profile IMA
16 Pages
MI 00 301
1 Page

Archived catalogs

*Prices are pre-tax. They exclude delivery charges and customs duties and do not include additional charges for installation or activation options. Prices are indicative only and may vary by country, with changes to the cost of raw materials and exchange rates.

Brand list