Mechanical Properties: The linear shafts made from X46CR13 (W.NR. 1.4034) exhibit mechanical properties as per the Peeled Hot Rolled EN 10088-3: 2005 standard. The tensile strength (R) ranges from 840 to 950 N/mm², with a yield strength (Rp 0.2) between 650 and 800 N/mm². The elongation (A%) is a minimum of 7, and the hardness (HB) ranges from 260 to 305.

Chemical Composition: The chemical analysis of the material includes Carbon (C) between 0.43% and 0.50%, Silicon (Si) up to 1.00%, Manganese (Mn) up to 1.00%, Phosphorus (P) up to 0.040%, Sulfur (S) up to 0.015%, and Chromium (Cr) between 12.5% and 14.5%, with specified tolerances.

Dimensional Specifications: The shafts are available in various diameters ranging from 8 mm to 50 mm, with corresponding weights from 0.4 Kg/m to 15.41 Kg/m. Lengths vary between 6000 mm and 6500 mm. Surface hardness is consistent at 53-55 HRC, with hardening depths varying by diameter. Straightness, roundness, and conicity are tightly controlled, with maximum deviations specified.

Surface Finish: The surface finish is maintained between 0.20 and 0.25 μ RA, ensuring a smooth and precise finish suitable for high-performance applications.

Manufacturer Information: The shafts are manufactured by HS Industries s.r.l., located in Pontirolo Nuovo, Italy. Contact details include phone numbers and an email address for inquiries.