Mechanical Properties: The linear shafts are made from X105CRMO17 (W.NR. 1.4125) and adhere to the Peeled Hot Rolled EN 10088-3: 2005 standard. Key mechanical properties include a tensile strength (R) of 760 N/mm², a yield strength (Rp 0.2) of at least 450 N/mm², an elongation (A%) of at least 14.00%, and a maximum hardness of 285 HB.

Dimensional Specifications: The shafts are available in various diameters ranging from 8 mm to 50 mm, with corresponding weights from 0.4 Kg/m to 15.41 Kg/m. Lengths vary between 6000 mm and 6500 mm. Surface hardness is between 53 and 55 HRC, with a hardening depth of 0.6 to 1.8 mm depending on the diameter. Straightness is maintained at a maximum of 4 mm/m, roundness at 3 μ max, and conicity at 3 μ max. Surface finish is specified between 0.20 and 0.25 μ RA.

Chemical Composition: The chemical analysis of the material includes carbon (C) content between 0.95% and 1.20%, silicon (Si) up to 1.00%, manganese (Mn) up to 1.00%, phosphorus (P) up to 0.040%, sulfur (S) up to 0.015%, chromium (Cr) between 16.0% and 18.0%, and molybdenum (Mo) between 0.40% and 0.80%.

Manufacturing Program: The document outlines the manufacturing program and tolerances, with diameter tolerances following ISO h6 standards.

Contact Information: HS Industries s.r.l. is located at Via Francesca Vecchia snc, 24040 Pontirolo Nuovo (BG), Italy. Contact can be made via phone at +39 0363 88 856 or +39 0363 88 817, fax at +39 0363 33 01 02, or email at [email protected]. More information is available on their website www.hs-industries.com.