Specifications:
- Film: Homogenous coloured PVC
- Film Thickness: 0.5 mm (Calliper Method)
- Total Applied Thickness: 0.57 mm (Calliper Method)
- Adhesive Type: Modified solvent acrylic
- Adhesive Thickness: 0.07 mm (Calliper Method)
- Peel Adhesion to Stainless Steel: 25.2 N/25mm (20 min dwell), 28.0 N/25mm (24 hr dwell) (FINAT FTM1)
- Tensile Strength: 158 N/25mm (Lloyd T5100 with 500N load cell)
- Elongation at Break: 294% (Lloyd T5100 with 500N load cell)
- Colour Options: Standard colours include black, orange, red, green, white, and yellow. Custom Pantone or RAL colours available based on MOQ.
- Temperature Range: -30ºC to +70ºC
- Maximum Roll Size: 1260mm x 100m

Friction Test Results:
- Dry Surface Pendulum Test: 102
- Wet Surface Pendulum Test: 24
- DIN51130: R10
Tests conducted at an independent friction testing laboratory.

Light Reflectance Value (LRV) Test Results:
- H6905R (Red): Av. LRV 15.38, Range 0.47
- H6905O (Orange): Av. LRV 23.07, Range 0.25
- H6905Y (Yellow): Av. LRV 52.33, Range 0.96
- H6905V (Green): Av. LRV 14.93, Range 0.78
- H6905B (Blue): Av. LRV 6.63, Range 0.4
- H6905W (White): Av. LRV 78.14, Range 0.78
- H6905N (Black): Av. LRV 3.13, Range 0.78
- H6905D (Black): Av. LRV 3.18, Range 0.75
- H6905D (Yellow): Av. LRV 62.88, Range 2.08
- H6905A (Red): Av. LRV 25.82, Range 1.14
- H6905A (White): Av. LRV 78.55, Range 1.93
Test procedure follows Lucideon In House Test Method WW22, compliant with BS.8493:2008+A1:2010.

All data is for reference only. Original test data available on request.