SE 85GT EPOXY PREPREG SYSTEM ¬ Highly impact resistant Rubber toughened system – excellent resistance to micro-cracking Controlled flow Good surface finishes possible Self adhesive – high peel strengths INTRODUCTION The SE 85GT series are toughened hot-melt, epoxy prepregs that offer an extremely good balance of mechanical properties. They are ideal for structural components where improved impact performance and resistance to resin microcracking is desired. SE 85GT can be cured at 80°C (176°F), yet remains an outlife of up to 56 days at 23°C (73°F). With its ¾ hour cure at 120°C (248°F), it is also suitable for quick manufacture of parts, and is also used in the development of trial components. SE 85GT has medium flow characteristics, so that heavy reinforcements can be easily wet out, and good consolidation can be achieved in very thick (>25mm) laminates, under just vacuum bag pressures. Its flow behaviour also means that it can produce excellent surface finishes when used in pressure-moulded components. SE 85GTBL is a black pigmented variant, often used in carbon fabrics to provide an excellent deep black gloss finish on the outer surface of carbon components such as yacht spars and race car parts. SE 85GT system can equally be used in sandwich structures with honeycomb and foam cores. In this application, depending on resin content, it can be used in a self-adhesive mode, although it is more commonly used in conjunction with the toughened SA 80 Adhesive Film (See separate datasheet).

Open the catalog to page 1

PROCESSING NOTES - GENERAL PROCESSING NOTES - CURING CURE CYCLES When preparing the lay-up the prepreg should be removed from the freezer and allowed to thaw in a sealed bag. This may take 6 to 24 hours depending on roll size. This prevents atmospheric moisture from condensing on the prepreg which may cause voiding on cure. The mould surface should be release coated and must have been tested for vacuum integrity prior to lay-up. For a good balance of composite properties, it is recommended that the laminate is cured at 85°C (185°F) for a minimum of 10 hours. A laminate may be cured in two...

Open the catalog to page 2

PRODUCT INFORMATION AVAILABILITY Small quantities of black pigmented version of SE 85GT on RC 200T and RC 280T4 are usually held in stock but other SE 85GT prepregs are available in a wide variety of fabric forms and collimated unidirectional tapes. Unidirectional materials are normally supplied on a single release paper and fabrics on a single polythene film. Please contact Customer Support to discuss specific requirements and availability. PREPREG PROPERTIES RHEOLOGY DATA TRANSPORT & STORAGE SE 85GT resin viscosity profile conducted at 1°C (1.8°F) per minute. When stored sealed & out of...

Open the catalog to page 3

LAMINATE PROPERTIES CURED LAMINATE PROPERTIES Cured using standard processing techniques and a fast cure time of 60 minutes at 125°C (248°F). PROPERTY TEST STANDARD Fabric / Fibre Description Woven 2x2 Twill HS Carbon Woven 4x4 Twill HS Carbon Resin Content Cure Method Cure Schedule Glass Transition Temperature 0° Comp. Str. Fibre Volume * 0° Compressive Strength (Normalised to 60%) 0° Flexural Fibre Volume * 0° GIIC Fibre Volume* 0° ILSS Fibre Volume* SACMA SRM1-94 ASTM D 3171 Method II * original laminate fibre volume fraction

Open the catalog to page 4

All advice, instruction or recommendation is given in good faith but the Company only warrants that advice in writing is given with reasonable skill and care. No further duty or responsibility is accepted by the Company. All advice is given subject to the terms and conditions of sale (the Conditions) which are available on request from the Company or may be viewed at the Company’s Website: www.gurit.com/terms-and-conditions.aspx. The Company strongly recommends that Customers make test panels and conduct appropriate testing of any goods or materials supplied by the Company to ensure that...