SC 110 COSMETIC CARBON PREPREG ¬ Ultra high clarity – ideal for cosmetic components with no white-wash or spots High-strength prepreg system Versatile process window with autoclave and press moulding 20 minute cure at 150°C (300°F) in a press Excellent tack allowing easy in-mould repositioning INTRODUCTION SC 110 is a cosmetic grade prepreg that utilises a high clarity, versatile, hot-melt epoxy resin formulation. The unique formulation ensures that no white-wash or spots are evident in the cured resin. It is ideal for manufacturing high visual quality components using autoclave and press moulding. It can be cured at temperatures as low as 80°C (175°F), or it can be used for faster moulding of components at 120°C (250°F). An even faster cure of 20 minutes at 150°C (300°F) can also be achieved using the appropriate press moulding technology. This is achieved whilst maintaining a good out-life of up to 3 weeks at 21°C (70°F). SC 110 is a toughened system, and offers excellent mechanical properties on a wide variety of reinforcing fabrics and fibres. During the development of SC 110, extensive beta testing has been conducted to manufacture the most challenging cosmetic components in order to demonstrate the robustness of the unique resin formulation. Tight curvature, resin rich seams and numerous components have been produced through autoclave and press moulding processes without any sign of white wash or spots. Gurit’s SC 110 is suitable for automotive, marine and any markets where a high clarity finish is required.

PRODUCT INFORMATION SC 110 cosmetic carbon prepreg is available in a range of product formats. Please consult your local sales contact for further information. Full contact details can be found at www.gurit.com. PREPREG PROPERTIES RHEOLOGY DATA TRANSPORT & STORAGE SC 110 resin viscosity profile conducted at 1°C (1.8°F) per minute. When stored sealed & out of direct sunlight. STORAGE TEMP Minimum Viscosity Temperature at Minimum Viscosity All prepreg materials should be stored in a freezer when not in use to maximise their useable life, since the low temperature reduces the reaction of resin and...

WOVEN LAMINATE Cured using standard processing techniques and a minimum cure time of 60 minutes at 120°C (250°F). PROPERTY Fabric / Fibre Description TEST STANDARD 245g/m2 2x2 twill fabric using T300 3k fibre 380g/m2 2x2 twill fabric using HSC 12k fibre Resin Content Cure Method Cure Schedule Glass Transition Temperature 0° Tensile Cured Fibre Volume** 0° Tensile Strength (Normalised to 60%) 0° Tensile Modulus (Normalised to 60%) 0° Compressive Str. Fibre Volume ** 0° Compressive Strength (Normalised to 60%) 0° Compressive Mod. Fibre Volume * 0° Compressive Modulus (Normalised to 60%) SACMA SRM1-94...

NOTICE All advice, instruction or recommendation is given in good faith but the Company only warrants that advice in writing is given with reasonable skill and care. No further duty or responsibility is accepted by the Company. All advice is given subject to the terms and conditions of sale (the Conditions) which are available on request from the Company or may be viewed at the Company’s Website: www.gurit.com/terms-and-conditions.aspx. The Company strongly recommends that Customers make test panels and conduct appropriate testing of any goods or materials supplied by the Company to ensure that...