Vertical system coatings Fast-drying HighSolid-Systems

Product catalog summary

Introduction
The document discusses a vertical coating system designed for the mechanical engineering industry, focusing on a HighSolid-Coating System that offers rapid drying times and excellent corrosion protection. The system combines a primer and top coat to enhance efficiency and performance.

Specifications
The EFDEDUR HighSolid-Primer UR1407 and EFDEDUR HighSolid coating UR1984 are developed to provide a highly adhesive and resistant coating system. The system is designed to dry quickly, with coated parts ready for packing within 60-90 minutes at room temperature. An oven can be used to further reduce drying time.

Product Details

HS Primer UR1407 and HS Top Coat UR1984 have a mixing ratio of 8:1 with curing agent HU0936.
Viscosity on delivery is 100-110 s for the primer and 70-75 s for the top coat.
Solids content is 78% for the primer and 76% for the top coat.
Both products have a pot life of 90 minutes at room temperature.

Approvals and Applications
Both systems are NSF approved for indirect contact with foodstuffs, making them suitable for machinery in the food industry. The coatings are highly adhesive, anti-corrosive, and durable, with the top coat resistant to various chemicals.

Chemical Resistance
The coatings show excellent resistance to chemicals such as super unleaded, diesel, antifreeze, gear oil, hydraulic oil, and more. The resistance is enhanced when the primer and top coat are used together.

Adhesion and Surface Compatibility
The coatings exhibit excellent adhesion to various surfaces, including steel, stainless steel, and aluminum. The cross-cut test results indicate strong adhesion with no significant changes.

Corrosion Protection
The system provides robust corrosion protection, suitable for both single-layer indoor applications and two-layer outdoor applications. The total layer thickness is approximately 200 μm after 1,000 hours of salt spray testing, with minimal creepage and subsurface corrosion.

Conclusion
The EFDEDUR HighSolid-Coating System offers a versatile and efficient solution for the mechanical engineering industry, providing rapid drying times, excellent adhesion, and strong corrosion resistance. For further inquiries, contact Emil Frei GmbH & Co. KG.

Catalog excerpts

Vertical system coatings Fast-drying HighSolid-Systems-1

Vertical system coatings Fast-drying HighSolid-Systems A vertical coating system combining primer and top coat was developed for the mechanical engineering industry with the goal of offering a HighSolid-Coating System with rapid drying times and excellent corrosion protection.

Open the catalog to page 1

Vertical system coatings Fast-drying HighSolid-Systems-2

Reduce throughput times with our high-solid coating system The EFDEDUR HighSolid-Primer UR1407 and EFDEDUR HighSolid coating UR1984 as a top coat were developed for the mechanical engineering industry with the goal of offering a brilliantly adhesive, resistant HighSolid coating system with excellent corrosion protection. Another main goal of the development was rapid drying. With a layer thickness of 50-70 pm (dry), the coated parts can be packed after just 60-90 minutes at room temperature. Optionally, an oven (up to 100 °C possible) can also be used to significantly shorten the drying time...

Open the catalog to page 2

Vertical system coatings Fast-drying HighSolid-Systems-3

Cross-cut test: Excellent adhesion to different surfaces + = No change 1 = Very little change 2 = Little (perceivable) change 3 = Moderate change (clearly perceivable) 4 = Large change 5 = Coating layer destroyed

Open the catalog to page 3

Vertical system coatings Fast-drying HighSolid-Systems-4

Suitable for use as either a single-layer or two-layer coating. Corrosion protection Thanks to its excellent resistance and general adhesion, EFDEDUR HighSolid-Coating UR1984 can also be used indoors as a single-layer coating. For higher stresses in outdoor areas, pre-priming should be performed by applying EFDEDUR HighSolidPrimer UR1407 or Epoxy-Resin FREOPOX-Primer ER1926. Structure: UR1407 with UR1984 Total layer thickness approx. 200 µm after 1,000 h SST Substrate: Smooth steel (left) Blasted steel (right) Creepage: <2 mm Subsurface corrosion: 1 mm No bubbles on surface or cut edge Also suitable...

Open the catalog to page 4

All FreiLacke | Emil Frei GmbH & Co. KG catalogs and technical brochures

Archived catalogs

Powder-coatings for Facade
4 Pages