Clear Photopolymer Resin Form 1+

Product catalog summary

Material Overview: Formlabs Clear Resin is designed for use with Form 1+ 3D Printers, producing strong, clear plastic parts suitable for various applications. It can be painted and finished to achieve high clarity. Post-curing enhances its tensile strength and stiffness beyond that of ABS materials.

Tensile Properties: The resin exhibits a tensile strength at yield of 29.82 MPa (green) and 61.53 MPa (post-cured), with a Young’s Modulus of 1.3 GPa (green) and 2.7 GPa (post-cured). Elongation at failure is 20% (green) and 5% (post-cured).

Flexural Properties: The flexural modulus is 0.97 GPa (green) and 2.38 GPa (post-cured).

Impact Properties: Notched IZOD impact strength is 22 J/m (green) and 29 J/m (post-cured).

Temperature Properties: Heat deflection temperature at 66 psi is 52 °C (green) and 78 °C (post-cured), while at 200 psi it is 47 °C (green) and 60 °C (post-cured). The temperature for 5% weight loss is 247 °C (green) and 274 °C (post-cured).

Notes: Material properties may vary based on part geometry, print orientation, settings, and temperature. Data for green parts was obtained using 50 µm Clear settings without additional treatments. Post-cured data was obtained after exposing green parts to 15 J/cm² of UV light.

Catalog excerpts

Photopolymer Resin for Form 1+ MATERIAL PROPERTIES Prepared: 06/09/2014 To the best of our knowledge the information contained herein is accurate. However, Formlabs, Inc. makes no warranty, expressed or implied regarding the accuracy of these results to be obtained from the use thereof.

Open the catalog to page 1

Formlabs Clear Resin produces strong plastic parts ideal for a wide variety of applications and is specifically designed to work with your Form 1+ 3D Printer. This material can be easily painted, and when the surface is finished or coated, produces a highly clear part. Upon post-cure, tensile strength and stiffness exceeds that of injection-molded or 3D-printed ABS. Tensile Properties Tensile Strength at yield Young’s Modulus Heat deflection temp. @ 66 psi Heat deflection temp. @ 200 psi Flexural Properties Flexural Modulus Impact Properties Notched IZOD Temperature Properties NOTES: 1 Material...

Open the catalog to page 2

Clear Photopolymer Resin Form 1+

Clear Photopolymer Resin Form 1+