General Properties:
Density of Polyamide (PA) ranges from 1.08 to 1.19 g/cm³ at 23°C. Water absorption is between 1% and 9% after 24 hours of saturation.

Thermal Properties:
The heat distortion temperature varies from 135-225°C at 0.46 MPa and 55-95°C at 1.82 MPa. The service temperature ranges from a minimum of -40°C to a maximum of 80°C for continuous use and 160°C for intermittent use.

Mechanical Properties:
Tensile strength at yield is between 45 and 95 MPa, with elongation at yield ranging from 3% to 30%. Elongation at break is between 5% and 150%. The tensile modulus is between 1600 and 3900 MPa, while the flexural modulus ranges from 2000 to 3000 MPa. Flexural strength is between 45 and 105 MPa. Izod impact strength (notched) is between 3 and 80 kJ/m² at 23°C, and Charpy impact strength (notched) is between 3 and 90 kJ/m² at 23°C.

Electrical Properties:
Dielectric strength ranges from 10 to 120 kV/mm, and volume resistivity is between 1E13 and 1E15 ohm.cm.

Flammability Properties:
The oxygen index is between 22 and 32, with a flammability rating of HB to V0 according to UL 94 standards.

Chemical Properties:
Polyamide shows poor resistance to both weak and strong acids, fair to bad resistance to weak and strong alkalis, good resistance to organic solvents, oils, and greases, and fair to bad resistance to UV and ozone exposure.

Document Information:
Issued by Moss Plastic Parts Ltd, authorized by F. Browne, Technical Quality Engineer, on 24/1/2000.

Catalog excerpts

ISOUNITCONDITIONSRESULTSGENERAL PROPERTIES Density1183g/cm323C1.08 Ж 1.19Water Absorption62%24h saturation1 - 9 THERMAL PROPERTIES Heat Distortion Temperature75C0.46/1.82MPa135-225 / 55-95Service temperatureMinimumаC-40Maximum (continuous/intermittent)C80 / 160 MECHANICAL PROPERTIES Tensile strength at yield527MPa45 Ж 95Elongation at yield527%3 - 30 Elongation at break527%5 150Tensile Modulus527MPa1600 - 3900Flexural modulus178MPa2000 ֖ 3000 Flexural Strength178MPa45 - 105 Izod Impact Strength (notched)180kJ/m223C3 Ж 80Charpy Impact Strength179kJ/m223C3 Ж 90(notched) ELECTRICAL PROPERTIES Dielectric StrengthIEC243kV/mm10 120VolumeResistivityIEC93ohm.cm1E13 ֖ 1E15 FLAMMABILITY PROPERTIES Oxygen index458922 - 32Flammability ratingUL 94HB V0 CHEMICAL PROPERTIES Resistance to Weak / Strong AcidsBad / BadResistance to Weak / Strong AlkalisFair / BadResistance to Organic SolventsGoodResistance to Oils and GreasesGood Resistance to UV / OzoneFair / Bad > TDS.DocMoss Plastic Parts Ltd,Issue: 01Langford Lane, Kidlington,Authorized:F.BrowneOxon, OX5 1HX.Technical Quality EngineerTel: +(44)(0) 1865 84 11 00 Date: 24/1/2000Fax: +(44)(0) 1865 37 01 35 size="-1">

Open the catalog to page 1

All Essentra Components catalogs and technical brochures

Archived catalogs

*Prices are pre-tax. They exclude delivery charges and customs duties and do not include additional charges for installation or activation options. Prices are indicative only and may vary by country, with changes to the cost of raw materials and exchange rates.

Brand list