Technical data sheet - TESNIT® BA-C TESNIT® BA-C TESNIT® BA-C gasket material with a vulcanized CSM matrix combines very good chemical and aging resistance, and low gas permeability. It can be used for sealing strongly acidic and alkaline solutions and gases, ozonized or chlorinated water, and the like. APPROPRIATE INDUSTRIES & APPLICATIONS  CHEMICAL INDUSTRY GENERAL PURPOSE  PAPER & CELLULOSE INDUSTRIES Aramid fibers, inorganic fillers, CSM binder Please inquiry Sheet dimensions Sheet size (mm): 1500 x 1500 Thickness (mm): 0.5 | 0.8 | 1.0 | 1.5 | 2.0 | 3.0 Other dimensions and thicknesses are available on request. Length and width: ± 5 % Thickness ≤ 1.0 mm: ± 0.1 mm Thickness > 1.0 mm: ± 10 % Surface finish Surface finish is 4AS. Optional graphite or PTFE finish on request TECHNICAL DATA Typical values for 2 mm thickness Density Compressibility Recovery Tesnile strength Residual stress At room temperature: εKSW 50 MPa, 175 °C, 16h 50 MPa, 300 °C, 16h Specific leak rate Thickness increase Oil IRM 903, 150 °C, 5 h ASTM Fuel B, 23°C, 5 h Compression modulus Creep relaxation At room temperature: εKRW DIN 28090-2 ASTM F36J ASTM F36J ASTM F1512 DIN 52913 Maximum operating conditions Peak temperature Continuous temperature Pressure °C/°F °C/°F bar/psi

Technical data sheet - TESNIT® BA-C EN 1514-1, Type IBC, PN 40, DIN 28091-2 / 3.8, 2 mm P-T diagrams indicate the maximum permissible combination of internal pressure and service temperature which can be simultaneously applied to a given gaskets thickness, size and tightness class. Given the wide variety of gasket applications and service conditions, these values should only be regarded as a guidance for the proper gasket assembly. In general, thinner gaskets exhibit better P-T properties. ■ General suitability applying common installation ■ practices under the condition of chemical compatibility....