Titan 8111

Titan 8111
2Pages

Catalog excerpts

TECHNICAL DATA SHEET Titan 8111 is a single component, low viscosity anaerobic threadlocking adhesive, which develops to high strength. Titan 8111 is used to lock and seal fine threaded nuts, bolts, and studs in a wide variety of applications. Physical Properties - Monomer (Uncured) Base Compound Appearance Dimethacrylate Ester Red liquid 17.5 +/- 7.5 cps Hot Strength (%RT strength, tested at temperature) Gap Fill Specific Gravity Flash Point Shelf Life Storage Condition RoHS-Compliant Physical Properties - Polymer (Cured) Appearance Locking Strength Service Temp Range Full Cure Time Pin/Collar Strength Red Solid High -65 to 300 °F 24 hours 2000 psi 14 N/mm2 Newton meters Breakaway Torque Prevailing Torque Setting Time / Full Cure Time* 20 30 55 60 minutes minutes minutes minutes Solvent Resistance Solvent Alcohol Ester (aromatic) Ethanol, Methanol Ketone (aromatic) Acetone, Benzophenone Benzyl, Toluol, Xylol Halogenated hydrocarbons Petrol, Heptanes, Hexane Aromatic hydrocarbons Aliphatic hydrocarbon (alkanes) Stainless Steel Heat Aging (aged at temp indicated and tested @ 22°C) Performance of Cured Adhesive Steel Brass Zinc-Plated Stainless Steel Methylenchloride, Chloroform, Chlorobenzol Weak aqueous acid Nitrite, muriatic acid, sulphuric acid, phosphoric acid Weak aqueous base sodium hydroxide solution, caustic potash

Open the catalog to page 1

General Instructions Surfaces to be bonded should be clean and dry and free of grease. Product should be applied in enough quantity to fill all engaged threads. The product performs best in thin bond gaps. Very large gaps may create gaps that will affect the cure speed and overall strength. Good contact is essential. An adequate bond develops in 15 to 45 minutes and maximum strength is attained in 24 hours. This product is not recommended for use in pure oxygen environments and/or oxygen-rich systems and should not be slected as a sealant for chlorine or other strong oxidizing materials....

Open the catalog to page 2