Polylite-PLA-Pro-EN_V5.3-1.pdf

Product catalog summary

Overview: Polylite™ PLA Pro is a professional-grade PLA filament that combines high toughness and rigidity, offering engineering properties with the ease of printing typical of regular PLA.

Specifications:

Density: 1.22 g/cm³ at 21.5°C (ISO1183, GB/T1033)
Melt Index: 6 g/10min at 210°C, 2.16 kg
Glass Transition Temperature: 62°C (DSC, 10°C/min)
Melting Temperature: 150°C (DSC, 10°C/min)
Vicat Softening Temperature: 62.7°C (ISO 306, GB/T 1633)
Heat Deflection Temperature: 57.6°C at 1.8MPa, 59.3°C at 0.45MPa (ISO 75)

Mechanical Properties:

Young’s Modulus: 2932.2 ± 55.3 MPa (X-Y), 2633.0 ± 117.4 MPa (Z)
Tensile Strength: 49.8 ± 0.4 MPa (X-Y), 36.5 ± 0.6 MPa (Z)
Elongation at Break: 6.3 ± 0.9% (X-Y), 2.4 ± 0.3% (Z)
Bending Modulus: 2933.8 ± 78.3 MPa (X-Y)
Bending Strength: 77.9 ± 0.4 MPa (X-Y)
Charpy Impact Strength: 17.1 ± 1.2 kJ/m² (X-Y)

Chemical Resistance: Not resistant to weak or strong acids and alkalis. No data available for organic solvents, oils, and grease.

Printing Parameters:

Nozzle Temperature: 190 – 220°C
Build Surface Material: BuildTak®, Glass, Blue Tape
Build Plate Temperature: 30 - 60°C
Cooling Fan: ON
Printing Speed: 30-70 mm/s
Environmental Temperature: 0 - 40°C
Recommended Support Material: PolySupport™ and PolyDissolve™ S1

Additional Notes: All specimens were conditioned at room temperature for 24 hours prior to testing. The document includes a disclaimer stating that the typical values are for reference only and actual values may vary significantly with printing conditions. Users are responsible for determining the suitability and safety of the material for their applications.

Catalog excerpts

Poly Ute™ PLA Pro Polylite™ PLA Pro is a first of its kind combining high toughness and high rigidity, this professional PLA offers engineering properties with the ease of print of regular PLA0 PHYSICAL PROPERTIES MOISTURE ABSORPTION CURVE

Open the catalog to page 2

WATER ABSORPTION % 0.1 Equilibrium water absorption (%)= 0.291

Open the catalog to page 3

Testing Method Glass transition temperature Melting temperature Crystallization temperature Decomposition temperature Vicat softening temperature Heat deflection temperature Heat deflection temperature Thermal conductivity Heat shrinkage rate

Open the catalog to page 4

TENS/LE TEST/NG SPECIMEN FLEXURAL TESTING SPECIMEN IMPACT TESTING SPECIMEN

Open the catalog to page 6

*All specimens were conditioned at room temperature for 24h prior to testing

Open the catalog to page 7

DISCLAIMER: The typical values presented in this data sheet are intended for reference and comparison purposes only. They should not be used for design specifications or quality control purposes. Actual values may vary significantly with printing conditions. End- use performance of printed parts depends not only on materials, but also on part design, environmental conditions, printing conditions, etc. Product specifications are subject to change without notice. Each user is responsible for determining the safety, lawfulness, technical suitability, and disposal/ recycling practices of Polymaker...

Open the catalog to page 8

All Bcn3d catalogs and technical brochures

Archived catalogs

*Prices are pre-tax. They exclude delivery charges and customs duties and do not include additional charges for installation or activation options. Prices are indicative only and may vary by country, with changes to the cost of raw materials and exchange rates.

Brand list