CarbonX™ Carbon Fiber Reinforced PETG 3D Filament
1Pages

Technology... Advanced. Technical Data Sheet Rev 2.1 CarbonX™ Carbon Fiber Reinforced PETG 3D Filament CarbonX™ Carbon Fiber Reinforced PETG [polyethylene terephthalate glycol copolymer] is a high-performance carbon fiber reinforced 3D printing filament. This grade was formulated utilizing high-modulus carbon fiber and premium PETG - making it ideal for applications that require superior stiffness, chemical resistance, and dimensional stability compared to any traditional unfilled FDM/FFF materials. Suitable for use in practically all consumer-grade FDM/FFF printers that have a heated print bed. Made by 3DXTECH® in the USA. The reported technical data was generated from printed ISO test specimen. The general print parameters utilized are noted below. • Desktop FDM/FFF Printer • Nozzle: 0.4mm A2 hardened • Layer height: 0.2mm • Infill: 100%, +/-45° • Extrusion temp: 240°C • Bed temp: 65°C • Bed prep: Hairspray on glass • Print speed: 50 mm/sec General Property Unit Standard Typical Value Mechanical Property Unit Standard Typical Value Tensile Strength MPa ISO 527 55.5 Tensile Modulus MPa ISO 527 4928 Tensile Elongation, Break % ISO 527 2.5 Flexural Modulus MPa ISO 178 5740 Flexural Strength MPa ISO 178 80 Thermal Property Unit Standard Typical Value Glass Transition Temperature [Tg] Heat Distortion Temperature [HDT] @ °C ISO 75 77 Electrical Property Unit Standard Typical Value Surface Resistivity Ohm/sq IEC 60093 >1010 Printing Recommendation Typical Range Extruder Temperature Print Speed WWW.3DXTECH.COM 571 Gordon Industrial Court, Suite E Byron Center, Ml 4931 5 USA