TELESCOPICSLIDES

Pre-galvanized (Sendzimir) Hot-dip zinc coating in accordance with EN 10326. Designation:Steel EN 10326-S320GD + Z100-M-C-O Layer thickness:Average 7 µm Corrosion resistance:1 hour neutral salt spray (DIN 50 021SS/ ASTM- B 117) before zinc corrosion occurs Bright Zinc Chromate,Blue passivation Coated in several colors Electrodeposited coating of zinc with trivalent blue passivation in accordance with NEN-EN 12329. Designation:prEN 12329-Fe/Zn5/B Layer thickness:Average 5 µm Corrosion resistance:72 hours neutral salt spray (DIN 50 021SS/ ASTM- B 117) before zinc corrosion occursA higher corrosion resistance is possible. For further information, please contact our sales department. Steel treated with iron-phosphate and water-borne polyester-melamine combination lacquer. Layer thickness:Average 10 µm Corrosion resistance:After 24 hours salt spray (DIN 50 021SS/ ASTM- B 117) maximum undermining of the coating 2-3mm out of scratch
PRODUCTRANGE

Thermal resistance

Maximum temperature approx. 100°C, determined by applied plastics and lubrication. Minimum temperature approx. -20°C, determined by applied plastics and lubrication. Attention: maximum and minimum temperature are strongly determined by the specificapplication; duration of exposure, impact and other forces on industrial slide and slide componentsetc. Values mentioned are indicative, it is important to judge each individual application. For special requests, please contact our sales department Content www.thomasregout.nl www.thomasrtegout.nl