| L-752 Laminating Prepreg, High Temperature Product Data Sheet | ||||||||||||||||||||||||||||||
| J.D. Lincoln inc. The Leader in Composite Material Technology 851 W. 18th Street Costa Mesa, CA 92627 (949) 650-8106 Fax:(949) 631-6190 www.jdlincoln.com | ||||||||||||||||||||||||||||||
| Revised: 12/20/06 | ||||||||||||||||||||||||||||||
| Description | ||||||||||||||||||||||||||||||
| L-752 is an excellent high temperature modified epoxy prepreg which exhibits outstanding performance at temperatures up to 400°F (204°C). L-752 is ideally suited for applications on light weight advanced aircraft for fairings, inlet ducting, leading edges, control surfaces, pylons, and radomes. | ||||||||||||||||||||||||||||||
| Advantages of L-752 | ||||||||||||||||||||||||||||||
| ❖ L-752 has an excellent balance between toughness, high temperature strength and weatherability. ❖ L-752 may be co-cured with many of today's graphite/epoxy prepreg systems to form load transfer interfaces. ❖ L-752 is also supplied on light weight aramid fabric for use as a surfacing ply for graphite/epoxy laminates and facesheets to improve their damage tolerance. | ||||||||||||||||||||||||||||||
| • Standard Weight: 0.070 lbs/ft2 (342 g/m2) • Standard Resin Content: 50% by weight | ||||||||||||||||||||||||||||||
| • Volatile Content: • Standard Tack: | Less than 0.5% Slightly tacky on one side | |||||||||||||||||||||||||||||
| • | ||||||||||||||||||||||||||||||
| Cured Ply Thickness: 0.010" (0.254 mm) • Other Weights, Resin Contents, and Fabrics are Available. | ||||||||||||||||||||||||||||||
| Availability | ||||||||||||||||||||||||||||||
| Up to 60" width in rolls up to 100 yards long (152 cm x 91 m) | ||||||||||||||||||||||||||||||
| m | ||||||||||||||||||||||||||||||
| Shelf Lif | ||||||||||||||||||||||||||||||
| 6 months at 40°F (4°C) or below 30 days at Room Temperature (70°F or 21°C) | ||||||||||||||||||||||||||||||