Mechanical Data

LAMINATE PROPERTIES PROPERTY25 PSI (0.17 MPa) CURE VACUUM BAG CURETESTMETHOD ULTIMATE TENSILE STRENGTH Room Temperature (RT) 60 KSI (414 MPa)54 KSI (372 MPa)ASTM D638 160°F(71°C)58 KSI (400 MPa)-ASTM D638 RT(WET)58 KSI (400 MPa)-ASTM D638 TENSILE MODULUS Room Temperature (RT) 3.5 MSI (24 GPa) 3.3 (23 GPa)ASTM D638 160°F(71°C)3.3 MSI (23 GPa) -ASTM D638 ULTIMATE COMPRESSION STRENGTH Room Temperature (RT) 22 KSI (152 GPa)20 KSI (138 GPa)ASTM D695 160°F(71°C)16 KSI (110 GPa)-ASTM D695 RT(WET)18 KSI (124 GPa)-ASTM D695 COMPRESSION MODULUS Room Temperature (RT) 3.2 MSI (22 GPa) 3.2 (22 GPa)ASTM D695 160°F(71°C)3.1 MSI (21 GPa) -ASTM D695 ULTIMATE FLEXURAL STRENGTH Room Temperature (RT) 55 KSI (349 MPa)-ASTM D790 160°F(71°C)42 KSI (290 MPa)-ASTM D790 FLEXURAL MODULUS Room Temperature (RT) 3.2 MSI (22 GPa) -ASTM D790 INTERLAMINAR SHEARSTRENGTH Room Temperature (RT) 2.2 KSI (15 MPa) -ASTM D2344
NOTICE: Product data and parameters cited in this publication have been obtained in J.D. Lincoln, Inc. laboratories using the materials under carefully controlled conditions. The information, therefore, is believed to be accurate and correctlystated. Data of this type maybe considered to be indicative of representative properties obtainable. J.D. Lincoln, Inc. cannot accept responsibility for the misapplication of these products, nor for their use under uncontrolled conditions. Numerical values resulting from the application of this material are dependant on processing details. It is recommended that the user develop his or her own application techniques and generate data consistent withhis or her specific application and process. L-701