Mechanical Data

LAMINATE PROPERTIES PROPERTY7781U.D. S-2 / 0°TESTMETHOD ULTIMATE TENSILE STRENGTH Room Temperature (RT) 62 KSI (428 MPa)172 KSI (1.2 GPa) ASTM D638 160°F(71°C)48 KSI (331 MPa)165 KSI (1.1 GPa) ASTM D638 TENSILE MODULUS Room Temperature (RT) 3.2 MSI (22 GPa) 7.5 MSI (52 GPa) ASTM D638 160°F(71°C)3.1 MSI (21 GPa) 7.5 MSI (52 GPa) ASTM D638 COMPRESSIVE STRENGTH Room Temperature (RT) 62 KSI (428 MPa)97 KSI (669 MPa)ASTM D695 COMPRESSIVE MODULUS Room Temperature (RT) 3.7 MSI (26 GPa) 8.3 MSI (57 GPa) ASTM D695 ULTIMATE FLEXURAL STRENGTH Room Temperature (RT) 85 KSI (586 MPa)175 KSI (1.2 GPa) ASTM D790 FLEXURAL MODULUS Room Temperature (RT) 4.0 KSI (28 MPa) 7.8 KSI (54 MPa) ASTM D790
NOTICE: Product data and parameters cited in this publication have been obtained in J.D. Lincoln, Inc. laboratories using the materials under carefully controlled conditions. The information, therefore, is believed to be accurate and correctlystated. Data of this type maybe considered to be indicative of representative properties obtainable. J.D. Lincoln, Inc. cannot accept responsibility for the misapplication of these products, nor for their use under uncontrolled conditions. Numerical values resulting from the application of this material are dependant on processing details. It is recommended that the user develop his or her own application techniques and generate data consistent withhis or her specific application and process. L-529