| | | MikroTest® | | |
| | | Magnetic coating thickness measurement | | |
| | | |
| | | |
| | | 7 | | |
| | | |
| | | The MikroTest® has been the most widely used coating thickness gauge in the world over the last 40 years. International patents and our industrial production "know-how" ensure that the gauge has the highest technical standards of all All instruments conform to national and international standards: DIN EN ISO 2178, DIN 50982, ASTM B 499, E 376, D 1186, G 12, B 530, BS 5411, ISO 2361 | | |
| | | Coating thickness standards for checking the accuracy of MikroTest | | |
| | | |
| | | |
| | | Application 11 Models - a MikroTest® for every application (see table) The balanced measuring system ensures accurate readings at any angle ■I Horizontal, vertical, overhead ■I The gauge allows measurements on curved surfaces ■I Precise measurements in tubes and on round parts due to the automatic operation Measuring principle The measurement of the coating thickness is based on magnetic attraction. The attractive force is related to the distance between a permanent magnet and a steel substrate. This dis- | | |
| | | tance represents the thickness of the coating to be measured. The magnet is lifted from the surface by means of a spring connected to the magnet arm. The force needed to lift the magnet is directly related to the angle of rotation of the torsion spring. This measuring principle is also especially suited for electroplated nickel on copper, aluminium and other non-ferrous metals. Technical data Features to make your quality control more precise and accurate ■I Highest accuracy with simplest operation ■I No calibration necessary Simple set-up and measurement ■I All gauges are without power or battery | | |
| | | ■I One point measurement ■I Robust metal case to protect from mechanical shocks ■I Precision measuring system resistant to solvents Useful accessories | | |
| | | |
| | | Belt pouch for industrial safe transport of the MikroTest® Wet film gauge for measuring the thickness of wet coatings Coating thickness standards for checking accuracy | | |
| | | ■I | | |
| | | |
| | | ■I | | |
| | | |
| | | ■I | | |
| | | |
| | | |
| | | Supply schedule ■I MikroTest® gauge with hand strap ■I Plastic carrying case ■I Operating instructions | | |
| | | |
| | | |
| | | Technical data | | |
| | | |
| | | Type | | R | | Application | | Tolerance* | | inimum surface | | Minimum curvature ra of the sample | | inimum base thickness | | |
| | | |
| | | |
| | | |
| | | | |
| | | |
| | | 0 20 mm 0 30 mm 0 30 mm 0 50 mm | | |
| | | 5/6 G 5/6 F 6 S3 6 S5 6 S10 6 S20 6 Ni50 6 Ni100 6 NiFe50 | | 0 ...100 um 0 ...1000 um 0.2.3 mm 0.5.5 mm 2.5. 10 mm 7.5.20 mm 0. 50 um 0. 100 um 0 . 50 um | | | 5 mm convex/ 25 mm concave 8 mm convex/ 25 mm concave 15 mm convex/ 25 mm concave 15 mm convex/ 25 mm concave | | 0.5 mm | | |
| | | Electroplating and paint coatings on steel** Paint on steel** | | um or 5% | | of reading | | |
| | | ± 1 | | |
| | | |
| | | |
| | | |
| | | |
| | | 0.5 mm 1.0 mm 1.0 mm | | |
| | | ±5 urn or 5% of reading ± 5% of reading ± 5% of reading ± 5% of reading ± 5% of reading ±(1 um + 5% of reading) ±(1 um + 5% of reading) ± (2 um + 8% of reading) 55 mm x 29 mm • Plastic carrying | | |
| | | |
| | | Enamel, plastic, rubber on steel** | | |
| | | |
| | | |
| | | |
| | | |
| | | | | |
| | | 0 50 mm 0 100 mm 0 15 mm 0 15 mm 0 20 mm | | 15 mm convex/ 25 mm concave 100 mm convex/150 mm concave 5 mm convex/ 25 mm concave 5 mm convex/ 25 mm concave 10 mm convex/ 25 mm concave | | 2.0 mm 7.0 mm | | |
| | | |
| | | electroplated nickel on non-ferrous substrates Electroplated nickel on steel** | | |
| | | CD ÇJ o £Z o '1 CD OÎ £Z CO u o œ CO CO £Z o "co ÇJ "c3 œ CP GO I— CD CD CNI \ LO CD CO < CT> CSI CO | | |
| | | 0.5 mm | | |
| | | | |
| | | |
| | | |
| | | Ambient temperature: -20°C...100°C • Dimensions: Gauge 215 mm x * Referring to ElektroPhysik standards ** Steel: ST 33 to ST 60 (Type 5 = Standard version, Type 6 = Automatic version) | | |
| | | case 235 mm x 185 mm x 46 mm • Weight: Case incl. gauge approx. 560 g | | |
| | | |
| | | |
| | | ElektroPhysik | | |
| | | |
| | | ElektroPhysik USA 770 West Algonquin Rd. Arlington Heights IL 60005 Phone: +1 847 437-6616 Fax: +1 847 437-00 53 www.elektrophysik.com epusa@elektrophysik.com | | |
| | | ElektroPhysik Pasteurstr. 15 D-50735 Köln Tel.: +49(0)221 7 5204-0 Fax: +49(0)221 7 5204-67 www.elektrophysik.com info@elektrophysik.com | | | ElektroPhysik Nederland Borgharenweg 140 6222 AA Maastricht Tel.: +31 (0)43/3 5200 60 Fax: +31 (0)43/3 631168 www.elektrophysik.com epnl@elektrophysik.com | | ElektroPhysik Belgium Rue Jouhaux 16 4102 Ougrée Tél.: +32(0)4 3365205 Fax: +32(0)4 3380180 www.elektrophysik.com epbe@elektrophysik.com | | |
| | | |
| | | |
| | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | |